    UNIVERSIDAD NACIONAL DE TRUJILLO

    SEMINARIO DE TESIS ING. ALCANTARA

    UNTUNIVERSIDAD NACIONAL DE TRUJILLO

    ESCUELA PROFESIONAL DE INGENIERA MECNICA

    ANALISIS DE LA INFLUENCIA QUE TIENE EL PROCESO DE COLORACIONSOBRE LOS ACEROS INOXIDABLES

    AUTOR1

    Alex Fernando Ruiz Juln2

    Luis Fernando Morales Arce3

    Edgar Lezama Hernandez4

    Edu Oliva Izaga5

    RESUMEN:

    Se ha investig la influencia que tiene el proceso de coloracin en los aceros inoxidables con elpropsito de aportar conocimientos sobre los mecanismos de informacin de los compuestos responsables de

    la coloracin y de la proteccin superficial que presenta.

    Se utilizaron probetas de acero inoxidable austentico AISI-304 de dimensiones de 4cm x 4cm y 2cmlas cuales se sumergieron en disolucin de cido sulfrico ?? utilizando un generador de funciones PROMAX

    GF232durante tiempos de 15, 30, 45 y 60 min utilizando el mtodo INCO para evaluar el grado de coloracin

    En la coloracin electroqumica

    los resultados obtenidos muestran que el espesor de la capa formada depende del tiempo de inmersinde la composicin y temperatura de disolucin y de la superficie a tratar . Los resultados muestran que a

    diferente tiempo y temperatura las intensidad de la coloracion varian. La temperatura ms aconsejable para

    realizar la electrolisis por corriente alterna estubo entre 70 y 80C dependiendo del color que se necesitedentro de la temperatura de 60C a tiempos cortos (15 y 30 min) el color conseguido no es muy intenso, por lo

    que es necesario trabajar a tiempos mayores del orden de 45 minutos.

    Se conculye que la tcnica de corriente alterna es la que mejor garantiza las propiedades de resistenciaa la corrosin

  • 7/27/2019 UNT (1)

    2/3

    UNTNATIONAL UNIVERSITY OF TRUJILLO

    PROFESSIONAL COURSE OF MECHANICAL ENGINEERING

    UNIVERSIDAD NACIONAL DE TRUJILLO

    SEMINARIO DE TESIS ING. ALCANTARA

    ANALYSIS OF THE INFLUENCE ON THE PROCESS OF COLOUR ON STAINLESS

    STEELAUTOR

    1

    Alex Fernando Ruiz Juln2

    Luis Fernando Morales Arce3

    Edgar Lezama Hernandez4

    Edu Oliva Izaga5

    Abstract:

    It has investigated the influence of the dyeing process in stainless steels in order to provide insights into themechanisms of information of the compounds responsible for the color and surface protection presented.

    Used austenitic stainless steel samples of AISI-304 dimensions 4cm x 4cm and 2cm which were immersed in

    sulfuric acid solution? Using a function generator GF232durante PROMAX with times of 15, 30, 45 and 60 min using themethod INCO, to evaluate the degree of coloration. In electrochemical coloration

    The results show that the thickness of the layer formed depends on the time of immersion, composition andtemperature of the solution and surface treated. The results show that at a different time and temperature the intensity ofthe coloration vary. The most suitable temperature for performing alternating current electrolysis Was between 70 and 80 C depending on the color that is needed, within a temperature of 60 C at short times (15 and 30 min) the colorobtained is not very intense, so it is necessary to work longer times of about 45 minutes.

    The technique conclude that AC is best properties ensures corrosion resistance

    Referencias:

  • 7/27/2019 UNT (1)

    3/3

    UNTNATIONAL UNIVERSITY OF TRUJILLO

    PROFESSIONAL COURSE OF MECHANICAL ENGINEERING

    UNIVERSIDAD NACIONAL DE TRUJILLO

    SEMINARIO DE TESIS ING. ALCANTARA

    1 Author of the Tesis project

    2 Mechanical Engineering Student, National University of Trujillo-Peruvian Citizen-Pueblo Nuevo town

    3 Mechanical Engineering Student, National University of Trujillo-Peruvian Citizen-Ciudad de Dios Town

    4 Mechanical Engineering student, National University of Trujillo-Peruvian citizen- Chepen town

    5 Mechanical Engineering student, National University of Trujillo-Peruvian citizen- Chepen town