Materiale invelitoare Sectiunea Kg /mp

Transm. Termica W / m2 C

Transmisia Luminii %

Izolatie Fonica

Rezistenta la impact J

Raza min. de

curbura

STICLÃ OBIªNUITÃ 4mm 9,6 5,8 100 2 - STICLÃ DUBLÃ 4mm+4mm 15,0 3,0 - PLEXIGLASS 4mm 4,8 5,3 85 12 Clar Opal 3B Opal 6B Bronz Albastru Vernil 4mm 2S

QUINN SPC

0,8 3,9 86 56 18 60 18dB 0,70m

6mm 2S

QUINN SPC

1,3 3,6 86 67 10 60 18dB 160 1,00m

8mm 2S

QUINN SPC

1,5 3,2 81 66 10 65 25 18dB 1,35m

10mm 2S

QUINN SPC

1,7 2,8 84 66 6 44 20dB 1,70m

10mm 4S

QUINN SPC

1,7 2,7 75 59 53 33 54 20dB 1,70m

16mm 3S QUINN SPC

2,7 2,3 73 45 25 20dB 2,70m

16mm XS

QUINN SPC

2.5 1.8 60 40 25 22dB 3.50m

20mm 3S QUINN SPC

3,2 2,0 73 34 22dB 3,30m

25mm XS QUINN SPC

3,3 1,5 57 41 15 22dB 5,30m

32mm XS optional

QUINN SPC

3,7 1,5 57 44 16 22dB 7,30m

35mm XS optional

QUINN SPC

4.0 1,4 56 44 16 22dB -

DATE TEHNICE

Proprietate Metodã U.M. QUINN SPC Densitate ISO 1183 G/cm 1,2 Duritate Rockwell D-78 Scala M - Proprietãþi optice Metodã U.M. QUINN SPC Transmisia luminii DIN 5036 % 86 Index de refracþie T3 N D 20 1,585 Proprietãþi mecanice Metodã U.M. QUINN SPC Modul de rezistenþã la încovoiere ISO 489 Mpa - Rezistenþã ISO 178 Mpa >95 Modul de rezistenþã la întindere ISO 527 Mpa 2200 Rezistenþã la întindere ISO 527 Mpa 60 Alungire ISO 527 % 80 Proprietãþi termice Metodã U.M. QUINN SPC Temperaturã Vicat (VST/B 50) ISO 306 °C 145 Temperatura de deformare la cãldurã (A) ISO R 75 °C 135 Capacitate caloricã specificã - J/gK 1,17 Coeficient de dilatare termicã liniarã DIN 53328 K-1x10-5 6,5 Conductivitate termicã DIN 52612 W/mK 0,2 Temperatura de degradare °C >280 Temperatura max. de exploatare cu utilizare continuã °C 115 Temperatura max. de exploatare cu utilizare de scurtã duratã °C 130 Domeniul termic de formare a plãcilor °C 180-210 Rezistenþa la ºoc Metodã U.M. QUINN SPC Probã Izod (cu crestãturã) ISO 180 KJ/m2 - Probã Charpy (cu crestãturã) ISO 179 KJ/m2 > 10 Probã Charpy (fãrã crestãturã) ISO 179 KJ/m2 NB Proprietãþi electrice Metodã U.M. QUINN SPC Constanta dielectricã la 50 Hz DIN 53483 3,0 Rezistivitatea de volum DIN 53482 1/2cm 1015 Rezistivitatea de suprafaþã DIN 53482 l 1015 Rigiditate dielectricã DIN 53481 KV/mm >30 Factor de disipare (50 Hz) DIN 53483 8x10-4

Acid acetic, 10% + Heptan + Acetonã - Hexan + Soluþii alcaline - Acid clorhidric concentrat - Amonic - Acid clorhidric, 20% + Sulfat de amoniu, soluþie apoasã saturatã

+ Acid fluorhidric concentrat

-

Benzen - Perhidrol, 30% + Acid benzoic - Metan + Acid boric + Alcool metilic - Acetat de butil - Metiletilcetonã - Alcool butiric + Clorurã de metilen - Clor gazos umed - Acid azotic, 10% + Acid cromic, 20 % + Ozon + Acid citric, 10% + Acid percloric, 10% +

Crezol - Hexacloretilen - Ciclohexanonã - Acid fosforic concentrat + Dibutilftalat - Permanganat de potasiu,

10% sol. Apoasã +

Eter etilic - Propan + Dietilenglicol + Acid propionic concentrat - Dimetilformamidã - Carbonat de sodiu, sol.

apoasã saturatã +

Dioctilftalat - Tetracloretan - Alcool etilic + Tetralinã - Etilenglicol + Xilen - Benzinã (fãrã hidrocarburi aromatice)

+

2

Comparaþie între DIFERITE MATERIALE

Kgm J

STICLA OBIªNUITÃ 4mm 0.2 2

STICLA ARMATÃ 6mm 1 10

PANOURI ACRILICE 1.2 12

POLICARBONAT CELULAR 6mm 16 160

POLICARBONAT COMPACT 2mm 20 120

Þara CLASA PRODUSUL TESTAT / numãr de pereti

FRANÞA M1 POLICARBONAT CELULAR 4mm/2 M2 POLICARBONAT CELULAR 6mm/2, 8mm/2, 10mm/2, 16mm/3, 20mm/3, 25mm/5,32mm/5 OLANDA CLASS 1 POLICARBONAT CELULAR 4mm-32mm POLONIA B 1 POLICARBONAT CELULAR 4-32mm ROMÃNIA C2 –DIFICIL

INFLAMABILE Toate produsele CELULARE ªI COMPACTE din POLICARBONAT în cazul utilizãrii lor cu celulele deschise ºi în pozitie verticalã

3

POLICARBONAT CELULAR

Raza Minima

POLICARBONAT COMPACT

Raza Minima

SPC 4mm 2S 700mm PC 2mm 300mm SPC 6mm 2S 1000mm PC 3mm 450mm SPC 8mm 2S 1500mm PC 4mm 600mm SPC 10mm 2S 1700mm PC 5mm 750mm SPC 10mm 4S 2000mm PC 6mm 900mm SPC 16mm TS 2700mm PC 8mm 1200mm SPC 16mm XS 3500mm PC 10mm 1500mm SPC 20mm 3S 3300mm PC 12mm 1800mm SPC 25mm XS 5300mm SPC 32mm XS 7300mm SPC 35mm XS 8400mm